Hanwha Total PP TB53
高结晶性聚丙烯
滑石填料
HANWHA TOTAL PETROCHEMICALS Co., Ltd.
产品说明：
TB53 is a heat-resistant polypropylene compound designed for use in injection molding, and features highly improved strength and heat resistance. TB53 is manufactured by adding an inorganic filler, talc to polypropylene, produced with a variety of base PPs, such as HIPP (High ***tactic or High Crystalline Polypropylene), SAC special processing technology results in the highest quality. This product features superior rigidity and impact strength, long-term heat resistance and anti-static property and dimensional stability. This SAC product is widely used in electric and electronic parts, household appliances and automobiles.
| 基本信息 |
|
|---|
| 黄卡编号 | |
| 填料/增强材料 | |
| 添加剂 | |
| 特性 | 尺寸稳定性良好 刚性，高 高强度 间苯二甲 抗静电性 抗撞击性，高 可加工性，良好 耐热性，高
|
| 用途 | 电气/电子应用领域 电气元件 电器用具 家用货品 汽车领域的应用 食品容器
|
| 形式 | |
| 加工方法 | |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 密度 | 1.16 | g/cm? | ASTM D1505 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (2.00 mm) | 0.80 到 1.2 | % | ASTM D955 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 洛氏硬度 (R 级) | 91 |
| ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 抗张强度 1(屈服) | 33.3 | MPa | ASTM D638 |
| 伸长率 2(断裂) | 60 | % | ASTM D638 |
| 弯曲模量 3 | 3430 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 (23°C) | 44 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 (0.45 MPa, 未退火) | 142 | °C | ASTM D648 |
| 可燃性 | 额定值 |
| 测试方法 |
|---|
| UL 阻燃等级 | HB |
| UL 94 |
| 注射 | 额定值 | 单位制 |
|
|---|
| 料筒后部温度 | 180 到 200 | °C |
|
| 料筒中部温度 | 190 到 210 | °C |
|
| 料筒前部温度 | 200 到 220 | °C |
|
| 模具温度 | 50.0 到 80.0 | °C |
|
| 注塑压力 | 39.2 到 88.3 | MPa |
|
| 保压 | 58.8 到 98.1 | MPa |
|
| 螺杆转速 | 30 到 80 | rpm |
|
| 备注 |
|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |